ASTM A36 Mild Steel Plates, which we deal in are comprehensively in demand due to their longer service life and low prices. They are fabricated in keeping in mind the laid industry norms.
More about ASTM A36 Mild Steel Plates :
ASTM A36 steel plates is a standard low carbon steel, without advanced alloying.
As with most steels, ASTM A 36 Steel plate has a density of 7,800 kg/m3 (0.28 lb/cu in). Young's modulus for A36 steel plate is 200 GPa (29,000,000 psi). A36 steel plate has a Poisson's ratio of 0.260, and a shear modulus of 79.3 GPa (11,500,000 psi).
A36 steel plates, ASTM a36 bars, and shapes with a thickness of less than 8 in (203 mm) has a minimum yield strength of 36,000 psi (250 MPa) and ultimate tensile strength of 58,000–80,000 psi (400–550 MPa). Plates thicker than 8 in have a 32,000 psi (220 MPa) yield strength and the same ultimate tensile strength.
A36 bars and shapes maintain their ultimate strength up to 650°F. Afterward, the minimum strength drops off from 58,000 psi: 54,000 psi at 700°F; 45,000 psi at 750°F; 37,000 psi at 800°F. A36 steel has low carbon that produce high strength to the alloys
Fabricated forms : A36 is produced in a wide variety of forms, including -
Methods of joinning
A36 is readily welded by nearly all welding processes. Therefore the ones most commonly used for A36 are those which are cheapest and easiest: shielded metal arc welding (SMAW, or stick welding), gas metal arc welding (GMAW, or MIG welding), and oxyacetylene welding.
A36 steel is also commonly bolted and riveted in structural applications.